Effects of dodecacalcium heptaaluminate content on the setting time, compressive strength, alkalinity, and cytocompatibility of tricalcium silicate cement

Authors

DOI:

https://doi.org/10.1590/1678-7757-2018-0247

Keywords:

Calcium silicate, Dental pulp, Physicochemical analysis, Material testing

Abstract

Objective: This study aimed to investigate the effects of dodecacalcium hepta-aluminate (C12A7) content on some physicochemical properties and cytocompatibility of tricalcium silicate (C3S) cement using human dental pulp cells (hDPCs). Material and Methods: High purity C3S cement was manufactured by a solid phase method. C12A7 was mixed with the cement in proportions of 0, 5, 8, and 10 wt% (C12A7-0, -5, -8, and -10, respectively). Physicochemical properties including initial setting time, compressive strength, and alkalinity were evaluated. Cytocompatibility was assessed with cell viability tests and cell number counts. Statistical analysis was performed by using one-way analysis of variance (ANOVA) and Tukey’s test (p<0.05). Results: The initial setting time of C3S-based cement was shorter in the presence of C12A7 (p<0.05). After 1 day, C12A7-5 showed significantly higher compressive strength than the other groups (p<0.05). After 7 days, the compressive strength of C12A7-5 was similar to that of C12A7-0, whereas other groups showed strength lower than C12A7-0. The pH values of all tested groups showed no significant differences after 1 day (p>0.05). The C12A7-5 group showed similar cell viability to the C12A7-0 group (p>0.05), while the other experimental groups showed lower values compared to C12A7-0 group (p<0.05). The number of cells grown on the C12A7-5 specimen was higher than that on C12A7-8 and -10 (p<0.05). Conclusions: The addition of C12A7 to C3S cement at a proportion of 5% resulted in rapid initial setting time and higher compressive strength with no adverse effects on cytocompatibility.

Downloads

Download data is not yet available.

Downloads

Published

2019-05-31

Issue

Section

Original Articles

How to Cite

Effects of dodecacalcium heptaaluminate content on the setting time, compressive strength, alkalinity, and cytocompatibility of tricalcium silicate cement. (2019). Journal of Applied Oral Science, 27, e20180247. https://doi.org/10.1590/1678-7757-2018-0247