Dental discoloration caused by Grey-MTAFlow cement: analysis of its physicochemical, biological and antimicrobial properties
DOI:
https://doi.org/10.1590/1678-7757-2020-0269%20Keywords:
Tooth discoloration, Dental materials, Bismuth, Zinc oxideAbstract
Tricalcium silicate-based cement are materials used in reparative and regenerative procedures in endodontics. A recently proposed formulation aimed to enhance handling during clinical use with a versatile material applicable by syringe. Although, the use of bismuth oxide as radiopacifier and grey raw powder are drawbacks considering aesthetics. Objectives: Evaluate physicochemical, biological, and antimicrobial properties of Grey-MTAFlow (Ultradent) and assess whether the addition of zinc oxide (ZnO) prevents dentinal discoloration caused by bismuth oxide. Methodology: Grey-MTAFlow was manipulated in 'thin' consistency for all tests. Luminosity, color change, ion migration to dentine, radiopacity, setting time, ISO 6876:2012 linear flow, volumetric lateral flow and central filling of simulated grooves scanned using micro-computed tomography (μCT), pH, calcium release, volumetric change using μCT, chemical characterisation, cytotoxicity, and antimicrobial activity were assessed. Addition of 5% ZnO to Grey-MTAFlow and a bismuth-containing experimental composition were comparatively tested. Statistical analyses used Shapiro-Wilk, T-test, ANOVA, and Kolmogorov-Smirnov (p<0.05). Results: The addition of ZnO to Grey-MTAFlow prevented dentine darkening after 90 days due to bismuth migration reduction, although no statistical difference was found (p=0.863). ZnO addition significantly enhanced Grey-MTAFlow radiopacity without differences in initial setting time. Grey-MTAFlow presented an ISO linear flow of 10.9 mm and a balanced volumetric lateral flow with central filling in μCT evaluation. All compositions presented an alkaline pH after immersion. Grey-MTAFlow had a significantly higher calcium ion release after 28 days in comparison to 24 hours (p=0.011) and volumetric expansion of 0.4±1.8% after immersion. ZnO addition altered the hydrated cement matrix once calcium hydroxide (portlandite) could not be detected in characterisation. Neither of the materials produced inhibition halos nor reduced bacterial turbidity, but all presented cytocompatibility above 100%.
Downloads
Downloads
Published
Versions
- 2021-09-03 (2)
- 2021-09-03 (1)
Issue
Section
License
Copyright (c) 2021 Journal of Applied Oral Science
This work is licensed under a Creative Commons Attribution 4.0 International License.
Todo o conteúdo do periódico, exceto onde está identificado, está licenciado sob uma Licença Creative Commons do tipo atribuição CC-BY.